1300 耐諾碳化鎢珠NanorWC由全球領先的的滴定滾動工藝成型，在真空電爐中無氧燒結而成。致
密的晶相結構造就了珠子至高的密度和耐磨性，是研磨介質微珠行業革命性的創造。
●Description:
NanorWC cemented carbide bead is shaped with cutting edge dropping
& rolling method from DURA and is sintered in the vacuum kiln. The
compact microstructure of bead offer the bead the highest density and
wear resistance. It is a creative invention of grinding media special
in small sizes.
●特 點：
★至高的密度：>14.0kg/dm3；
★超高的硬度：>1500kg/mm2；
★穩定性佳：耐酸堿，耐高溫。
●Features:
—Highest density: >14.0kg/dm3 ,
—Super hardness: >1500kg/mm2,
—Super stability: acid & alkali resistance, high temperature
resistance .
●應用領域：
★超硬材料的研磨：氧化鋁、氮化硼、碳化硅、氮化硅和碳化鎢等材料；
★納米行業：高密度的碳化鎢微珠能完成高效的能量的傳遞，保證物料無污染的納米級研磨。
●Applications：
—For high hard material grinding: alumina, boron nitride, silicon nitride, silicon
carbide, tungsten carbide and other material.
—Nano-grinding and dispersion: higher energy transmit of small sizes of NanorWC bead guarantee
nanometer grinding in free contamination.
●化學組成 Chemical Composition：
|
成 分 |
WC |
Co |
|
Wt% |
≈85% |
≈15% |
●物理性質 Typical Properties：
|
比 重 Specific Gravity |
散 重 Bulk Density |
莫氏硬度 Hardness Mohs |
維 氏 硬 度 Hardness Vickers |
耐壓強度 Crushing Strength |
斷裂韌性 Fracture Toughness |
彈性模量 Elasticity Module |
|
≥14.3kg/dm3 |
≥8.5kg/L |
9.5 |
>1500kg/mm2 |
>220kgf(2mm) |
> 15MPa.m1/2 |
>710GPa/2 |
●規 格 Sizes：
|
型號 Code |
粒徑（φmm） sizes |
|
型號 Code |
粒徑（φmm） Sizes |
|
NW2 |
0.2 |
|
NW8 |
0.8～1.0 |
|
NW3 |
0.3 |
|
NW10 |
1.0～1.2 |
|
NW4 |
0.4 |
|
NW12 |
1.2～1.4 |
|
NW5 |
0.4～0.6 |
|
NW14 |
1.4～1.6 |
|
NW6 |
0.6～0.8 |
|
NW16 |
1.6～1.8 |